GLASS THE THICKNESS OF THE MATERIAL LOWEST PUBLISHED ESTIMATED NM POINT ESTIMATED NM POINT LAST PUBLISHED
GENERIC CODE ORIGIN THE GENERAL SOURCE AVAILABILITY USED TO GENERATE THE PUBLISHED TRANSMISSION OCCURRING WHERE TRANSMISSION WHERE TRANSMISSION TRANSMISSION IN
 -----  ------ ALPHA CODE USED CATALOG  ------ NM TRANSMISSION VALUES IN OR NEAR APPROACHES "~" 50%  APPROACHES "~" 90%  THE IR SPECTRUM THAT KNOOP YIELD EXPANSION  DENSITY DENSITY
PER  MANUFACTURER OR IN THE COUNTRY DATE P=PREFERRED/AVAIL. PROVIDED ON THE THE UV SPECTRUM IS 90% OR GREATER HARDNESS (DEFORMATION)   COEFFICIENT  GM/CM^3  LB./IN^3
MIL-STD. COUNTRY INDICATED OR FOR THE EG=ECOLOGICAL THE REFERENCED LINE  -----  -----  ----- (SEE MFTR. TEMPERATURE ( X 10^-7)
G-174-B  ------ AS THE  LINE  H = HISTORICAL  -----  ----- ASCENDING FROM OR  ASCENDING FROM UV  DESCENDING FROM UV-VIS, DESCRIPTION) DEGREES C  -30 / +70
INDICATED  I = INQUIRY EXCEPTION: "*" INDICATES THAT  "~<"= 1% TRANSMISSION NEAR THE UV REGION REGION & NEAR-IR REGIONS DEGREES C
 ----- (SEE MFTR. MANUFACTURER'S  ----- NA = NOT AVAILABLE THE VALUES WERE DERIVED FOR A IS AT OR BELOW  -----  -----   -----
MIL. CODE=NNNVVV DESCRIPTION) TRADEMARK EXCEPTION:  ----- HYPOTHETICAL  1MM THICK  NM POINT GIVEN
 ----- CALCULATED DERIVED = NOT MATERIAL USING A   ----- "~<"= 50% TRANS. PT. "~<"= 90% TRANS. PT. "~>"= 90% TRANS. PT. IS
CONVERSION: DERIVATION= THE MANUFACTURER'S LOGARITHM DENSITY FORMULA.  (XX%) TRANSMISSION BELOW NM PT. GIVEN- BELOW NM PT. GIVEN- BEYOND NM PT. GIVEN-
nd=1.+NNN NOT FROM PUBLISHED VALUES- HOYA'S SOURCE DATA WAS USED AT THE (XX%) TRANS. AT THE (XX%) TRANS. AT THE  (XX%) TRANS. AT THE 
vd=VV.V A  HYPOTHETICAL TO ILLUSTRATE THE THEORETICAL NM POINT INDICATED NM POINT INDICATED NM POINT INDICATED NM POINT INDICATED
CATALOG EFFECTS OF A THICKNESS CHANGE. SEE SEE SEE SEE SEE
*SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* *SEE DISCLAIMER* DISCLAIMER DISCLAIMER DISCLAIMER DISCLAIMER DISCLAIMER
600425 HOYA CORP. BaFD16 1978 H / I 5MM  -----  -----  -----  ----- 615 91 2.58 0.093
601382 SCHOTT GLASS TECH. F14 1992 I 5MM ~310nm ~327nm ~345nm ~>700nm (99.8%) 380  ----- 79 3.44 0.125
601510 RUSSIA C392 PRE 1992 H / I 10MM ~<320 (21.4%) ~338 ~378 ~>1500 (96.5%) ----- 40 2.95 0.107
603379 RUSSIA C322 PRE 1992 H / I 10MM ----- ----- ~<400 (97.9%) ~>1500 (99.4%) ----- 70 3.48 0.126
603380 CHINA F1 1996 H / I ----- ----- ----- ----- ----- 445 87 3.43 0.124
603380 HIKARI GLASS CO. E-F5 2001 EG/P 10MM ~<360(13%) ~369 ~389 ~>2400(90%) 635 622  ----- 2.65 0.096
603380 HOYA CORP. EF5 DERIVED  HYPOTHETICAL 1MM*  ----- ~<350 (63.1%) ~365 ~>1550 (99.9%) 515 80 2.63 0.095
603380 HOYA CORP. EF5 1998 P/EG 5MM ~<350 (10%) ~361 ~379 ~>1550 99.7%) 515 80 2.63 0.095
603380 HOYA CORP. F5 DERIVED  HYPOTHETICAL 1MM*  ----- ~<320 (74.1 %) ~329 ~>1550 (99.9%) 445 89 3.45 0.125
603380 HOYA CORP. F5 1998 P 5MM ~<320 (23%) ~327 ~344 ~>1550 (99.7%) 445 89 3.45 0.125
603380 OHARA CORP. PBM5 1990 I 10MM ~<320 (10%) ~332 ~356 ~>700 (99.8%) 420 88 3.44 0.125
603380 OHARA CORP. S-TIM5 1996 P/EG 10MM ~<360 (19%) ~368 ~387 ~>2200 (92.3%) 540 83 2.63 0.095
603380 SCHOTT GLASS TECH. F5 2000 H / I 10MM ~<320 (9%) ~332 ~356 ~>1970 (95.9%) 450  ----- 80 3.47 0.126
603380 SCHOTT GLASS TECH. F5 1992 P 5MM ~<310 (2%) ~326 ~347 ~>2325.4 (93%) 380 80 3.47 0.126
603381 HIKARI GLASS CO. F5 2001 I 10MM ~<320 (11%) ~329 ~347 ~>700 (99.9%) 386 474  ----- 3.45 0.125
603423 OHARA CORP. BAM25 1990 I 10MM ~<320 (5%) ~333 ~355 ~>1060 (99.7%) 460 84 3.46 0.125
603424 HOYA CORP. BaFD5 1978 H / I 5MM ~<310 (6%) ~328 ~350 ~>700 (99.9%) 485  ----- 3.48 0.126
603425 CHINA BAF51 1996 H / I ----- ----- ----- ----- ----- 400 68 3.49 0.126
603425 EAST GERMANY BaSF5 PRE 1992 ACQ. BY SCHOTT 10MM ~320 ~345 ~382 ~>1500 (98.5%) ----- 79 3.49 0.126
603425 SCHOTT GLASS TECH. BaSF5 1992 H / I 5MM ~<320 (20%) ~327 ~345 ~>700 (99.8%) 400 688 79 3.49 0.126
603437 OHARA CORP. BAM4 1990 H / I 10MM ~<330 (18%) ~339 ~362 ~>1060 (99.6%) 450 80 3.50 0.127
603606 CHINA ZK14 1996 H / I ----- ----- ----- ----- ----- 515 59 3.44 0.125
603606 PILKINGTON OPTICAL   DBC603606 1990 H / I 10MM  ----- ~<360 (86.4%) ~368 ~>1000 (99.5%) 550 63 3.44 0.125
603606 PILKINGTON OPTICAL   DBC603606A 2002 EG 5MM  ----- ~<360 (96.8%) ~>2200.0 (92.2%) 563 60 3.42 0.124
603606 SCHOTT GLASS TECH. NSK14 2000 P/EG 10MM ~<290 (4%) ~318 ~349 ~>1970 (95.9%) 600 60 3.44 0.125
603606 SCHOTT GLASS TECH. SK14 1992 H / I 5MM ~<280 (6%) ~306 ~340 ~>1970.1 (95.4%) 490 773 60 3.44 0.125
603607 HIKARI GLASS CO. E-SK14 2001 EG/P 10MM ~<290(3%) ~316 ~347 ~>700(99.9%) 574 694  ----- 3.43 0.124
603607 HOYA CORP. BACD14 DERIVED  HYPOTHETICAL 1MM*  ---- ~<290 (63.1%) ~320 ~>1550 (99.9%) 585 60 3.43 0.124
603607 HOYA CORP. BaCD14 1998 P 5MM ~<290 (8%) ~315 ~345 ~>1550 (99.6%) 585 60 3.43 0.124
603607 OHARA CORP. BSM14 1990 H / I 10MM ~<290 (2%) ~323 ~355 ~>700 (99.7%) 580 60 3.44 0.125
603607 OHARA CORP. S-BSM14 1996 P/EG 10MM ~310 ~322 ~349 ~>2200 (91.9%) 570 62 3.43 0.124
603654 SCHOTT GLASS TECH. PSK52 1992 I 5MM ~<320 (8%) ~350 ~387 ~>1970.1 (96.0%) 450  ----- 85 3.38 0.122
603655 HIKARI GLASS CO. E-PSK03 2001 EG/P 10MM ~<300(2%) ~336 ~367 ~>2000(95.4%) 316 641  ----- 3.52 0.127
603655 OHARA CORP. PHM53 1990 H / I 10MM ~<310 (3%) ~343 ~374 ~>700 (99.7%) 390 93 3.51 0.127
603655 OHARA CORP. S-PHM53 1996 P/EG 10MM ~<310 (3%) ~343 ~374 ~>2000 (94.1%) 390 93 3.51 0.127
604381 CORNING-FRANCE C04-38 1991 P 10MM ~<310 (5%) ~328 ~350 ~>1800 (96.7%)  ----- 598 81 3.46 0.125
604382 EAST GERMANY F5 PRE 1992 ACQ. BY SCHOTT 10MM ~<320 (3%) ~337 ~368 ~>1500 (99.4%) ----- 80 3.46 0.125
604536 SCHOTT GLASS TECH. SSK51 1992 I 5MM ~320 ~339 ~361 ~>2325.4 (93%) 470 771 76 3.28 0.119
604606 RUSSIA C117 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 61 3.44 0.125
604610 EAST GERMANY SK14 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 49 3.44 0.125
604640 CORNING-FRANCE C04-64 1991 P 10MM ~<320 (10%) ~355 ~385 ~>1800 (96.9%)  ----- 607 91 3.67 0.133
605380 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.49 0.126
605380 HAYWARD SCIENTIFIC DF1 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
605434 HAYWARD SCIENTIFIC BF2 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
605436 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.52 0.127
606378 SCHOTT GLASS TECH. F15 1992 I 5MM ~<310 (2%) ~327 ~347 ~>700 (99.9%) 390 598 81 3.48 0.126
606379 HOYA CORP. F15 1978 H / I 5MM ~<310 (9%) ~328 ~345 ~>700 (99.9%) 425  ----- 3.45 0.125
606437 OHARA CORP. S-BAM4 1996 P/EG 10MM ~<350 (6%) ~363 ~384 ~>2200 (91.9%) 520 84 2.91 0.105
606438 HIKARI GLASS CO. E-BAF4 2001 EG/P 10MM ~<350(2%) ~365 ~383 ~>2200 (92.5%) 482 638  ----- 2.89 0.105
606439 CHINA BAF5 1996 H / I ----- ----- ----- ----- ----- 475 72 3.50 0.127
606439 CORNING-FRANCE C06-44 1991 P 10MM ~<340 (3%) ~360 ~385 ~>1800 (97.8%)  ----- 694 88 2.80 0.101
606439 EAST GERMANY BaF4 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (28.0%) ~350 ~388 ~>1500 (99.0%) ----- 79 3.50 0.127
606439 HOYA CORP. BaF4 1978 H / I 5MM ~<320 (15%) ~330 ~355 ~>700 (99.9%) 475  ----- 3.50 0.127
606439 PILKINGTON OPTICAL   BF606439 1990 H / I 10MM  ------ ~<360 (94.5%) ~<360 (94.5%) ~>1000 (99.8%) 480 82 3.48 0.126
606439 SCHOTT GLASS TECH. BaF4 1992 I 5MM ~<320 (15%) ~334.1 (72%) ~347 ~>2325.4 (93%) 400 694 79 3.50 0.127
606439 SCHOTT GLASS TECH. N-BAF4 2000 P   -----
606440 HOYA CORP. MBaF41 DERIVED  HYPOTHETICAL 1MM*  ---- ~<360 (84.7%) ~365 ~>1550 (99.9%) 380  ---- 2.89 0.105
606440 HOYA CORP. MBaF41 1998 P 5MM ~<350 (6%) ~362 ~382 ~>1550 (99.8%) 380  ----- 2.89 0.105
607403 EAST GERMANY BaSF3 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (44.0%) ~343 ~376 ~>1500 (99.7%) ----- 80 3.51 0.127
607403 OHARA CORP. BAM23 1990 I 10MM ~<320 (10%) ~331 ~355 ~>1060 (99.8%) 420 89 3.48 0.126
607404 HOYA CORP. BaFD3 1978 H / I 5MM  -----  -----  -----  ----- 475 79 3.50 0.127
607440 RUSSIA C246 PRE 1992 H / I 10MM ~<340 (45.3%) ~342 ~370 ~>1500 (99.1%) ----- 75 3.46 0.125
607492 OHARA CORP. BAM5 1990 I 10MM ~<320 (4%) ~337 ~364 ~>1060 (99.7%) 500 81 3.39 0.123
607493 EAST GERMANY BaF5 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (30.3%) ~349 ~383 ~>1500 (98.7%) ----- 79 3.54 0.128
607493 HOYA CORP. BaF5 1978 H / I 5MM ~<320 (6%) ~335 ~365 ~>700 (99.9%) 540  ----- 3.52 0.127
607494 CHINA ----- 1996 H / I ----- ----- ----- ----- ----- 450 68 3.54 0.128
607494 SCHOTT GLASS TECH. BaF5 1992 H / I 5MM ~<310 (5%) ~327 ~349 ~>2325.4 (95%) 450 765 70 3.54 0.128
607550 HOYA CORP. BaCD50 1978 H / I 5MM  -----  -----  -----  ----- 635 66 2.90 0.105
607566 CORNING-FRANCE C07-57 1991 P 10MM ~<310 (28.0%) ~320 ~349 ~>1800 (98.9%)  ----- 825 60 3.55 0.129
607567 CHINA ZK50 1996 H / I ----- ----- ----- ----- -----  -----  -----  -----  -----
607567 EAST GERMANY SK2 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 65 3.52 0.127
607567 HOYA CORP. BaCD2 DERIVED  HYPOTHETICAL 1MM*  ----- ~<310 (87.1%) ~324 ~>1550 (99.9%) 570 63 3.53 0.128
607567 HOYA CORP. BaCD2 1998 P 5MM ~<300 (3%) ~310 ~348 ~>1550 (99.7%) 570 63 3.53 0.128
607567 PILKINGTON OPTICAL   DBC607567 1990 H / I 10MM  ------  -----  ------  ----- 510 65 3.53 0.128
607567 PILKINGTON OPTICAL   DBC607567A 2002 EG 5MM  ------ ~<320 (78.3%) ~335 ~>2200.0 (93.8%) 507 62 3.54 0.128
607567 SCHOTT GLASS TECH. NSK2 2000 P 10MM ~<290 (2%) ~320 ~349 ~>1970 (97.1%) 550 60 3.55 0.129
607567 SCHOTT GLASS TECH. SK2 1992 H / I 5MM ~<280 (3%) ~309 ~340 ~>2325.4 (95.2%) 550 823 60 3.55 0.129
607568 HIKARI GLASS CO. E-SK2 2001 EG/P 10MM ~<290(1%) ~323 ~355 ~>2200(90.8%) 466 664  ----- 3.45 0.125
607568 OHARA CORP. BSM2 1990 H / I 10MM ~<300 (7%) ~319 ~348 ~>700 (99.7%) 540 63 3.54 0.128
607568 OHARA CORP. S-BSM2 1996 P/EG 10MM ~<310 (4%) ~328 ~353 ~>2200 (95.1%) 560 65 3.53 0.128
607594 OHARA CORP. BSM7 1990 I 10MM ~<290 (7%) ~324 ~356 ~>700 (99.7%) 540 65 3.51 0.127
607595 CHINA ZK15 1996 H / I ----- ----- ----- ----- ----- 520 62 3.51 0.127
607595 HAYWARD SCIENTIFIC DBC8 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
607595 HOYA CORP. BaCD7 1978 H / I 5MM ~<290 (5%) ~320 ~350 ~>700 (99.9%) 580 63 3.52 0.127
607595 PILKINGTON OPTICAL   DBC607595 1990 H / I 10MM  ------ ~<360 (88.0%) ~365 ~>1000 (99.1%) 560 62 3.37 0.122
607595 SCHOTT GLASS TECH. SK7 1992 I 5MM ~<290 (9%) ~307 ~338 ~>2325.4 (93%) 570 772 64 3.51 0.127
608461 RUSSIA C243 PRE 1992 H / I 10MM ~<340 (30.2%) ~350 ~387 ~>1500 (98.5%) ----- 66 3.47 0.126
608462 CHINA BAF6 1996 H / I ----- ----- ----- ----- ----- 530 75 3.50 0.127
608462 EAST GERMANY BaF7 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (38.7%) ~346 ~378 ~>1500 (99.0%) ----- 78 3.54 0.128
608462 HOYA CORP. BaF7 1978 H / I 5MM  -----  -----  -----  ----- 530  ----- 3.50 0.127
608652 RUSSIA C040 PRE 1992 H / I 10MM ~<340 (14.0%) ~379 ~395 ~>1500 (99.3%) ----- 87 3.62 0.131
609464 SCHOTT GLASS TECH. BaF52 1992 I 5MM ~<334.1 (11%) ~348 ~365.0 ~>2325.4 (94%) 440 697 84 3.32 0.120
609466 SCHOTT GLASS TECH. NBAF4  -----  -----  -----  -----  -----  -----  -----  -----  -----  -----  -----
609466 SCHOTT GLASS TECH. NBAF52 2000 P/EG 10MM ~<350 (5%) ~364 ~389 ~>1970 (95.4%) 600 69 3.05 0.110
609589 CHINA ZK4 1996 H / I ----- ----- ----- ----- ----- 570  ----- 3.52 0.127
609589 HOYA CORP. BaCD3 1978 H / I 5MM ~<300 (3%) ~327 ~358 ~>700(99.9%) 570 74 3.54 0.128
609589 SCHOTT GLASS TECH. SK3 1992 I 5MM ~<300 (3%) ~322 ~348 ~>2325.4 (95.9%) 560 777 63 3.53 0.128
609590 CORNING-FRANCE C09-59 1991 P 10MM ~<280 (9%) ~320 ~350 ~>1800 (98.4%) 498 745 64 3.52 0.127
609590 OHARA CORP. BSM3 1990 H / I 10MM ~<300 (5%) ~325 ~357 ~>700 (99.7%) 530 66 3.53 0.128
610375 HAYWARD SCIENTIFIC DF5 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
610565 OHARA CORP. BSM1 1990 H / I 10MM ~<300 (2%) ~323 ~352 ~>700 (99.7%) 540 66 3.57 0.129
610567 HOYA CORP. BaCD1 1978 H / I 5MM ~<280 (6%) ~315 ~345 ~>700 (99.9%) 560 73 3.56 0.129
610567 PILKINGTON OPTICAL   DBC610567 1990 H / I 10MM  ------  -----  -----  ----- 550 63 3.56 0.129
610567 SCHOTT GLASS TECH. SK1 1992 I 5MM ~<300 (12%) ~317 ~347 ~>2325.4 (95.6%) 560 786 61 3.56 0.129
610573 PILKINGTON OPTICAL   DBC610573 1990 H / I 10MM  ------ ~<360 (91.4%) ~<360 (91.4%) ~>1000 (99.8%)  ----- 63 3.56 0.129
611558 CHINA ZK5 1996 H / I ----- ----- ----- ----- ----- 560 61 3.58 0.130
611558 HOYA CORP. BaCD8 1978 H / I 5MM ~<310 (16%) ~325 ~350 ~>700 (99.9%) 560 65 3.58 0.130
611558 RUSSIA C109 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 59 3.58 0.130
611559 OHARA CORP. BSM8 1990 H / I 10MM ~<310 (3%) ~335 ~365 ~>700 (99.6%) 520 63 3.57 0.129
611559 SCHOTT GLASS TECH. SK8 1992 H / I 5MM ~<300 (5%) ~318 ~345 ~>700 (99.9%) 540  ----- 60 3.57 0.129
611572 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.57 0.129
611572 HAYWARD SCIENTIFIC DBC3 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
611588 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.58 0.130
611588 HAYWARD SCIENTIFIC DBC1 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
612441 CHINA TF3 1996 H / I ----- ----- ----- ----- ----- 430 46 3.23 0.117
612441 RUSSIA C389 PRE 1992 H / I 10MM  ---- ~340 ~377 ~>1500 (92.5%) ----- 48 3.15 0.114
612450 HAYWARD SCIENTIFIC BF6 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
612595 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.45 0.125
613370 CHINA F2 1996 H / I ----- ----- ----- ----- ----- 440 89 3.50 0.127
613370 EAST GERMANY F3 PRE 1992 ACQ. BY SCHOTT 10MM  ----- ~340 ~373 ~>1500 (99.7%) ----- 64 3.55 0.129
613370 HIKARI GLASS CO. E-F3 2001 EG/P 10MM  ----  ----  ----  ---- 482 637  ----- 2.67 0.097
613370 HOYA CORP. EF3 DERIVED  HYPOTHETICAL 1MM*  ---- ~<350 (63.1%) ~366 ~>1550 (99.9%) 540 77 2.64 0.096
613370 HOYA CORP. EF3 1998 P/EG 5MM ~<350 (7%) ~362 ~380 ~>1550 (99.7%) 540 77 2.64 0.096
613370 HOYA CORP. F3 DERIVED  HYPOTHETICAL 1MM*  ----- ~<320 (70.4%) ~330 ~>1550 (99.9%) 440 87 3.54 0.128
613370 HOYA CORP. F3 1998 P 5MM ~310 (6%) ~327 ~344 ~>1550 (99.7%) 440 37 3.54 0.128
613370 OHARA CORP. PBM3 1996 I 10MM ~<320 (5%) ~332 ~348 ~>2400 (91.7%) 410 83 3.53 0.128
613370 OHARA CORP. S-TIM3 1999 P/EG 10MM ~<360 (13%) ~369 ~389 ~>2400 (91.3%) 510 77 2.67 0.097
613370 RUSSIA C316 PRE 1992 H / I 10MM ~<340 (37.6%) ~346 ~377 ~>1500 (99.6%) ----- 71 3.57 0.129
613370 SCHOTT GLASS TECH. F3 1992 I 5MM ~<320 (30%) ~325 ~343 ~>2325.4 (93%) 360 602 80 3.55 0.129
613438 OHARA CORP. BPM4 1990 I 10MM ~<320 (7%) ~347 ~382 ~>1060 (99.7%) 420 53 3.22 0.117
613440 EAST GERMANY KzFS1 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (4%) ~369 ~403 ~>1500 (98.0%) ----- 53 3.16 0.114
613442 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.18 0.115
613442 OHARA CORP. BPM51 1990 H / I 10MM ~<310 (2%) ~340 ~376 ~>1060 (99.8%) 420 52 3.24 0.117
613443 CHINA TF4 1996 H / I ----- ----- ----- ----- ----- 565 39 3.21 0.116
613443 HOYA CORP. ADF40 1978 H / I 5MM  -----  -----  -----  ----- 435 56 3.20 0.116
613443 OHARA CORP. BPM51 1996 I 10MM ~<310 (3%) ~336 ~372 ~>2000 (92.4%) 420 52 3.24 0.117
613443 OHARA CORP. S-NBM51 1999 I 10MM ~<320 (8%) ~331 ~355 ~>2000 (97.2%) 570 65 2.93 0.106
613443 PILKINGTON OPTICAL   BORF613443 1990 H / I 10MM  ------  -----  -----  ----- 420 51 3.20 0.116
613443 SCHOTT GLASS TECH. KzFS1 1992 I 5MM ~<300 (4%) ~334.1 ~380 ~>700 (99.8%) 370 547 50 3.14 0.114
613443 SCHOTT GLASS TECH. KzFSN4 1992 P 5MM ~<310 (20%) ~320 ~352 ~>1970.1 (95.8%) 380 594 45 3.20 0.116
613444 CORNING-FRANCE C13-44 1991 NA 10MM ~<340 (43%) ~345 ~370 ~>1000 (99.3%) 513  -----  ---- 3.01 0.109
613444 HOYA CORP. ADF10 DERIVED  HYPOTHETICAL 1MM*  ---- ~<290 (63.1%) ~311 ~>700 (99.9%) 370  ----- 3.15 0.114
613444 HOYA CORP. ADF10 1998 P 5MM ~<290 (8%) ~307 ~348 ~>700 (99.9%) 370  ----- 3.15 0.114
613444 HOYA CORP. EADF10 DERIVED  HYPOTHETICAL 1MM*  ----- ~<340 (78.6%) ~349 ~>1550 (99.6%) 445  ----- 3.04 0.110
613444 HOYA CORP. EADF10 1998 P/EG 5MM ~<330 (6%) ~346 ~370 ~>1550 (98.1%) 445  ----- 3.04 0.110
613445 SCHOTT GLASS TECH. NKZFS4 2000 P/EG 10MM ~<320 (4%) ~335 ~362 ~>1970 (96.5%) 520 73 3.00 0.109
613449 HOYA CORP. ADF4 1978 H / I 5MM ~<340 (8%) ~355 ~380 ~>700 (99.9%) 460 44 3.44 0.125
613574 OHARA CORP. BSM19 1990 H / I 10MM ~<310 (4%) ~335 ~364 ~>700 (99.7%) 560 66 3.59 0.130
613574 SCHOTT GLASS TECH. SK19 1992 H / I 5MM ~<300 (12%) ~315 ~347 ~>2325.4 (91%) 500  ----- 64 3.56 0.129
613584 CHINA ZK6 1996 H / I ----- ----- ----- ----- ----- ----- 3.56 0.129
613584 RUSSIA C121 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 66 3.56 0.129
613585 CORNING-FRANCE C13-58 1991 P 10MM ~<285 (3%) ~323 ~356 ~>1800 (97.9%)  ----- 730 63 3.59 0.130
613586 EAST GERMANY SK4 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 63 3.56 0.129
613586 HOYA CORP. BaCD4 DERIVED  HYPOTHETICAL 1MM*  ----- ~<300 (70.4%) ~323 ~>1550 (99.9%) 560 66 3.58 0.130
613586 HOYA CORP. BaCD4 1998 P 5MM ~<290 (4%) ~317 ~342 ~>1550 (99.6%) 560 66 3.58 0.130
613586 PILKINGTON OPTICAL   DBC613586 1990 H / I 10MM  ------ ~<360 (83.1%) ~372 ~>1000 (99.3%) 550 76 3.56 0.129
613586 PILKINGTON OPTICAL   DBC613586A 2002 EG 5MM  ----- ~<320 (76.0%) ~340 ~>2200.0 (93.8%) 566 66 3.56 0.129
613586 SCHOTT GLASS TECH. NSK4 2000 P/EG 10MM ~<320 (10%) ~333 ~361 ~>1970 (95.9%) 580 65 3.54 0.128
613586 SCHOTT GLASS TECH. SK4 1992 I 5MM ~<300 (6%) ~319 ~349 ~>2325.4 (95.0%) 580 767 64 3.57 0.129
613587 HIKARI GLASS CO. E-SK4 2001 EG/P 10MM ~<290(1%) ~328 `355 ~>2200(94.4%) 598 696  ----- 3.54 0.128
613587 OHARA CORP. S-BSM4 1996 P/EG 10MM ~<310 (4%) ~329 ~357 ~>2200 (91.1%) 560 67 3.57 0.129
613588 OHARA CORP. BSM4 1990 H / I 10MM ~<300 (6%) ~324 ~354 ~>700 (99.7%) 560 66 3.55 0.129
613595 HAYWARD SCIENTIFIC DBC10 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
613606 CHINA ZK7 1996 H / I ----- ----- ----- ----- ----- 560 64 3.56 0.129
613606 RUSSIA C119 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 63 3.51 0.127
614346 RUSSIA C327 PRE 1992 H / I 10MM ----- ~<380 (79.5%) ~397 ~>1500 (99.0%) ----- 90 2.93 0.106
614400 CHINA BAF7 1996 H / I ----- ----- ----- ----- ----- 400 70 3.56 0.129
614400 RUSSIA C239 PRE 1992 H / I 10MM ~<340 (29.9%) ~349 ~378 ~>1050 (99.5%) ----- 71 3.56 0.129
614439 PILKINGTON OPTICAL   BORF614439 1990 H / I 10MM  ------ ~<360 (69.7%) ~380 ~>1000 (99.3%)  ----- 58 3.25 0.118
614550 OHARA CORP. BSM9 1996 H / I 10MM ~<310 (3%) ~328 ~355 ~>2200 (93.9%) 530 61 3.60 0.130
614550 OHARA CORP. S-BSM9 1999 P/EG 10MM ~<330 (3%) ~347 ~370 ~>2200 (94.0%) 560 64 3.22 0.117
614551 CHINA ZK8 1996 H / I ----- ----- ----- ----- ----- 525 61 3.49 0.126
614551 HOYA CORP. BaCD9 1978 H / I 5MM  -----  -----  -----  ----- 565 60 3.58 0.130
614551 RUSSIA C111 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 62 3.61 0.131
614552 EAST GERMANY SK9 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 73 3.60 0.130
614552 SCHOTT GLASS TECH. SK9 1992 I 5MM ~<310 (11%) ~324 ~350 ~>700 (99.8%) 480  ----- 60 3.60 0.130
614563 EAST GERMANY SK6 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 50 3.59 0.130
614564 CHINA ZK19 1996 H / I ----- ----- ----- ----- ----- 470 65 3.60 0.130
614564 CORNING-FRANCE C13-56 1991 P 10MM ~315 ~335 ~365 ~>1800 (97.9%)  ----- 740 63 3.58 0.130
614564 HOYA CORP. BaCD6 1978 H / I 5MM ~<290 (5%) ~319 ~350 ~>700 (99.9%) 540 70 3.59 0.130
614564 OHARA CORP. BSM6 1990 I 10MM ~300  ~327 ~355 ~>700 (99.7%) 520 66 3.60 0.130
614564 SCHOTT GLASS TECH. SK6 1992 I 5MM ~290 ~324 ~355 ~>2325.4 (92%) 550 788 62 3.60 0.130
615512 HOYA CORP. BaCED3 1978 H / I 5MM ~<320 (22%) ~330 ~355 ~>700 (99.9%) 460  ----- 3.60 0.130
615512 OHARA CORP. BSM23 1990 I 10MM ~<340 (9%) ~355 ~384 ~>700 (99.5%) 500 71 3.45 0.125
615512 SCHOTT GLASS TECH. SSK3 1992 I 5MM ~<310 (3%) ~327 ~348 ~>2325.4 (95.0%) 460 773 66 3.61 0.131
616444 CORNING-FRANCE C16-44 1991 P 10MM ~<300 (3%) ~346 ~383 ~>1800 (94.6%)  ----- 581 47 3.14 0.114
617310 CHINA TIF4 1996 H / I ----- ----- ----- ----- ----- 300 173 3.31 0.120
617310 SCHOTT GLASS TECH. TiF6 1992 H / I 5MM ~<365.0 (3%) ~377 ~400 ~>1529.6 (99.0%) 310 494 139 2.79 0.101
617366 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.64 0.132
617366 CHINA F3 1996 H / I ----- ----- ----- ----- ----- 430 78 3.57 0.129
617366 EAST GERMANY F4 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (48.7%) ~341 ~374 ~>1500 (99.5%) ----- 64 3.57 0.129
617366 HAYWARD SCIENTIFIC DF2 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
617366 HOYA CORP. F4 1978 H / I 5MM ~<320 (14%) ~330 ~355 ~>700 (99.9%) 430  ----- 3.57 0.129
617366 OHARA CORP. PBM4 1990 I 10MM ~<320 (3%) ~336 ~359 ~>1060 (99.8%) 400 86 3.58 0.130
617366 RUSSIA C318 PRE 1992 H / I 10MM ----- ~<360 (75.8%) ~380  ~>1100 (99.6%) ----- 70 3.60 0.130
617366 SCHOTT GLASS TECH. F4 2000 P 10MM ~<320 (3%) ~334 ~357 ~>1970 (95.0%) 420  ----- 83 3.58 0.130
617385 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.61 0.131
617385 HAYWARD SCIENTIFIC BF1 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
617539 CHINA ZK20 1996 H / I ----- ----- ----- ----- ----- 475 61 3.63 0.131
617539 HOYA CORP. BaCED1 1978 H / I 5MM ~<320 (21%) ~330 ~355 ~>700 (99.9%) 565 63 3.63 0.131
617539 SCHOTT GLASS TECH. SSK1 1992 I 5MM ~<310 (10%) ~326 ~350 ~>2325.4 (95.0%) 450 759 63 3.63 0.131
617540 OHARA CORP. BSM21 1990 10MM ~<320 (8%) ~338 ~368 ~>700 (99.7%) 520 63 3.63 0.131
617541 EAST GERMANY SSK1 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 70 3.62 0.131
617541 RUSSIA C113 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 68 3.62 0.131
617549 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.66 0.133
617550 HAYWARD SCIENTIFIC DBC2 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
617551 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.36 0.122
617628 HOYA CORP. PCD5 1978 H / I 5MM  -----  -----  -----  ----- 455 107 3.50 0.127
617628 OHARA CORP. PHM51 1990 H / I 10MM ~<310 (8%) ~338 ~368 ~>1060 (99.9%) 450 97 3.53 0.128
617628 OHARA CORP. S-PHM51  ----- I  ----  ------  -----  -----  ----- 450 97 3.53 0.128
618498 CHINA ----- 1996 H / I ----- ----- ----- ----- ----- ----- 3.33 0.121
618498 HIKARI GLASS CO. E-SSK8 2001 EG/P 10MM ~<340(3%) ~358 ~384 ~>2200(93%) 483 642  ----- 3.22 0.117
618498 OHARA CORP. BSM28 1990 H / I 10MM ~<340 (5%) ~357 ~386 ~>1060 (99.1%) 490 84 3.25 0.118
618498 OHARA CORP. S-BSM28 1996 P/EG 10MM ~<340 (2%) ~359 ~387 ~>2200 (94.4%) 540 84 3.23 0.117
618498 SCHOTT GLASS TECH. NSSK8 2000 P 10MM ~<350 (19%) ~361 ~387 ~>1970 (95.9%) 570 72 3.27 0.118
618498 SCHOTT GLASS TECH. SSKN8 1992 I 5MM ~<334.1 (14%) ~346 ~368 ~>2325.4 (92%) 460 730 71 3.33 0.121
618504 EAST GERMANY SSK7 PRE 1992 ACQ. BY SCHOTT 10MM ~<360 (18.0%) ~375 ~412 ~>1500 (98.2%) ----- 79 3.35 0.121
618526 SCHOTT GLASS TECH. SSK50 1992 I 5MM ~320 ~353 ~376 ~>2325.4 (94%) 480 746 74 3.42 0.124
618551 CORNING-FRANCE C17-55 1991 P 10MM ~302 ~334 ~362 ~>1800 (97.7%)  ----- 741 62 3.56 0.129
618551 EAST GERMANY SSK4 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 68 3.61 0.131
618551 OHARA CORP. BSM24 1990 H / I 10MM ~<320 (3%) ~342 ~372 ~>1060 (99.1%) 520 65 3.63 0.131
618551 SCHOTT GLASS TECH. SSK4 1992 I 5MM ~<310 (13%) ~322 ~345 ~>2325.4 (94%) 460 791 61 3.63 0.131
618552 HOYA CORP. BaCED4 1978 H / I 5MM ~<310 (7%) ~328 ~358 ~>700 (99.9%) 575 61 3.62 0.131
618634 HIKARI GLASS CO. E-PSK02 2001 EG/P 10MM ~<320 (1%) ~354 ~382 ~>2000(96.3%) 355 652  ----- 3.55 0.129
618634 HOYA CORP. PCD4 DERIVED  HYPOTHETICAL 1MM*  ----- ~<280 (82.7%) ~306 ~>1550 (99.9%) 445 92 3.52 0.127
618634 HOYA CORP. PCD4 1998 P 5MM ~<280(38%) ~295 ~344 ~>1550(99.6%) 445 92 3.52 0.127
618634 OHARA CORP. PHM52 1990 H / I 10MM ~<330 (6%) ~348 ~373 ~>1060 (99.8%) 420 102 3.67 0.133
618634 OHARA CORP. S-PHM52 1996 P/EG 10MM ~<330 (5%) ~350 ~380 ~>2200 (92.6%) 390 101 3.67 0.133
620363 CHINA F50 1996 H / I ----- ----- ----- ----- ----- 425 84 3.60 0.130
620363 CORNING-FRANCE C20-36 1991 P 10MM ~<320 (6.3%) ~336 ~357 ~>1800 (96.6%) 360 548 85 3.60 0.130
620363 HIKARI GLASS CO. E-F2 2001 EG/P 10MM ~<360(5%) ~374 ~396 ~>2400(90.7%) 531 640  ----- 2.69 0.097
620363 HIKARI GLASS CO. F2 2001 I 10MM ~<320 (1%) ~335 ~350 ~>700 (99.9%) 413 477  ----- 3.61 0.131
620363 HOYA CORP. EF2 DERIVED  HYPOTHETICAL 1MM*  ----- ~<360 (82.7%) ~367 ~>1550 (99.9%) 530 83 2.67 0.097
620363 HOYA CORP. EF2 1998 P/EG 5MM ~<350 (6%) ~363 ~383 ~>1550 (99.8%) 530 83 2.67 0.097
620363 HOYA CORP. F2 DERIVED  HYPOTHETICAL 1MM*  ---- ~<320 (63.1%) ~333 ~>1550 (99.9%) 425 83 3.60 0.130
620363 HOYA CORP. F2 1998 P 5MM ~<320 (11%) ~330 ~347 ~>1550 (99.8%) 425 83 3.60 0.130
620363 OHARA CORP. PBM2 1990 I 10MM ~<320 (2%) ~335 ~356 ~>1060 (99.9%) 420 87 3.60 0.130
620363 OHARA CORP. S-TIM2 1996 P/EG 10MM ~<360 (8%) ~372 ~394 ~>2200 (93.0%) 550 81 2.69 0.097
620364 CHINA F4 1996 H / I ----- ----- ----- ----- ----- 390 70 3.58 0.130
620364 EAST GERMANY F2 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (45.1%) ~343 ~376 ~>1500 (99.5%) ----- 77 3.61 0.131
620364 PILKINGTON OPTICAL   DF620364 1990 H / I 10MM  ------ ~<360 (89.1%) ~363 ~>1000 (99.8%) 410 89 3.63 0.131
620364 PILKINGTON OPTICAL   DF620364A 2002 EG 5MM  ----- ~<330 (75.4%) ~<360 (94.2%) ~>2200.0 (94.4%) 417 85 3.61 0.131
620364 RUSSIA C329 PRE 1992 H / I 10MM ~<340 (28.8%) ~350 ~382 ~>1500 (99.4%) ----- 71 3.63 0.131
620364 SCHOTT GLASS TECH. F2 2000 P 10MM ~310 ~333 ~350 ~>1970 (95.4%) 420  ----- 82 3.61 0.131
620364 SCHOTT GLASS TECH. NF2 2000 P/EG 10MM ~<350 (10%) ~371 ~391 ~>1970 (95.0%) 600 78 2.65 0.096
620381 HOYA CORP. F9 1978 H / I 5MM ~<330 (16%) ~340 ~360 ~>700 (99.9.%) 435  ----- 3.56 0.129
620381 OHARA CORP. PBM9 1990 I 10MM ~<330 (10%) ~344 ~372 ~>1060 (99.7%) 460 80 3.56 0.129
620381 SCHOTT GLASS TECH. F9 1992 I 5MM  ----- ~334.1 (50%) ~350 ~>2325.4 (93%) 400 625 77 3.56 0.129
620494 EAST GERMANY D362 PRE 1992 ACQ. BY SCHOTT 10MM ~<360 (27.1%) ~371 ~400 ~>1500 (98.9%) ----- 82 3.26 0.118
620496 OHARA CORP. BSM29 1990 H / I 10MM ~340  ~362 ~392 ~>700 (99.6%)  520 84 3.24 0.117
620498 CHINA ZBAF11 1996 H / I ----- ----- ----- ----- ----- 450 80 3.27 0.118
620498 HOYA CORP. BaCED9 1978 H / I 5MM ~<340 (16%) ~355 ~380 ~>700 (99.9%) 555  ----- 3.27 0.118
620598 HOYA CORP. BaCD165 1978 H / I 5MM  -----  -----  -----  ----- 540  ----- 3.61 0.131
620600 HAYWARD SCIENTIFIC DBC7 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
620601 SCHOTT GLASS TECH. SK55 1992 I 5MM ~<280 (5%) ~311 ~347 ~>1970.1 (97.7%) 550 700 60 3.35 0.121
620603 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.58 0.130
620603 CHINA ZK9 1996 H / I ----- ----- ----- ----- ----- 565 60 3.52 0.127
620603 CORNING-FRANCE C20-60 1991 P 10MM ~<290 (5%) ~334 ~365 ~>1800 (95.9%) 487 738 69 3.60 0.130
620603 EAST GERMANY SK16 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 53 3.60 0.130
620603 HIKARI GLASS CO. E-SK16 2001 EG/P 10MM ~<290(2%) ~322 ~353 ~>2200(92%)  ---- 688  ----- 3.60 0.130
620603 HOYA CORP. BaCD16 DERIVED  HYPOTHETICAL 1MM*  ----- ~<290 (67.6%) ~318 ~>1550 (99.9%) 575 60 3.52 0.127
620603 HOYA CORP. BaCD16 1998 P 5MM ~<280 (3%) ~315 ~345 ~>1550 (99.5%) 575 60 3.52 0.127
620603 OHARA CORP. BSM16 1990 H / I 10MM ~<300 (3%) ~325 ~358 ~>700 (99.7%) 550 66 3.57 0.129
620603 OHARA CORP. BSM16C 1990 I 10MM ~<290 (2%) ~324 ~358 ~>700 (99.8%) 530 63 3.57 0.129
620603 OHARA CORP. S-BSM16 1996 P/EG 10MM ~310 ~330 ~357 ~>2200 (91.1%) 570 67 3.59 0.130
620603 PILKINGTON OPTICAL   DBC620603 1990 H / I 10MM  ----- ~<360 (89.0%) ~363 ~>1000 (99.7%) 540 71 3.60 0.130
620603 PILKINGTON OPTICAL   DBC620603A 2002 EG 5MM  ------ ~<330 (77.7%) ~346 ~>2200.0 (93.0%)  -----  ----- 3.61 0.131
620603 PILKINGTON OPTICAL   DBC620603B 2003 EG 5MM  ----- ~<320 (68.1%) ~350 (90.8%) ~>2200.0 (91.9%) 577 61 3.50 0.127
620603 SCHOTT GLASS TECH. NSK16 2000 P/EG 10MM ~290 ~325 ~356 ~>1970 (95.0%) 600 63 3.58 0.130
620603 SCHOTT GLASS TECH. SK16 1992 H / I 5MM ~<290 (5%) ~317 ~350 ~>1970.1 (97.4%) 490 750 63 3.58 0.130
620622 HOYA CORP. ADC1 DERIVED  HYPOTHETICAL 1MM*  ---- ~<320 (63.1%) ~344 ~>700 (99.9%) 350 109 3.88 0.140
620622 HOYA CORP. ADC1 1998 P 5MM ~<320 (7%) ~340 ~363 ~>700 (99.9%) 350 109 3.88 0.140
620622 HOYA CORP. ATC1 1978 H / I 5MM  -----  -----  -----  ----- 350 109 3.88 0.140
620635 HOYA CORP. PCD53 1978 H / I 5MM  -----  -----  -----  ----- 435 112 3.57 0.129
620635 SCHOTT GLASS TECH. NPSK53 2000 P/EG 10MM ~<334 (24%) ~343 ~367 ~>1970 (95.0%) 440 94 3.60 0.130
620635 SCHOTT GLASS TECH. PSK53A 1992 H / I 5MM ~<320 (7%) ~334.1 ~361 ~>700 (99.8%) 440  ----- 94 3.60 0.130
621359 OHARA CORP. PBM11 1990 H / I 10MM ~<360 (5%) ~375 ~399 ~>1060 (99.7%) 530 75 2.66 0.096
621359 OHARA CORP. TIM11  ----- I  -----  -----   ---------  ----  ------ 530 75 2.66 0.096
621360 EAST GERMANY F11 PRE 1992 ACQ. BY SCHOTT 10MM ~<360 (3%) ~377 ~405 ~>1500 (99.2%) ----- 75 2.66 0.096
621360 HOYA CORP. F11 1978 H / I 5MM ~<350 (6%) ~368 ~390 ~>700 (99.9%) 620  ----- 2.67 0.097
621362 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.67 0.133
621362 CHINA ----- 1996 H / I ----- ----- ----- ----- ----- ----- 2.66 0.096
621362 HAYWARD SCIENTIFIC DF3 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- -----
621362 SCHOTT GLASS TECH. FN11 1992 H / I 5MM ~<350 (2%) ~363 ~379 ~>2325.4 (92%) 510 691 75 2.66 0.096
621603 SCHOTT GLASS TECH. SK51 2000 P 10MM  -----  -----  -----  -----  -----  -----  -----  -----  -----
622360 SCHOTT GLASS TECH. F13 1992 I 5MM ~<320 (20%) ~328 ~347 ~>2325.4 (92%) 370 604 87 3.62 0.131
622531 CHINA ZBAF1 1996 H / I ----- ----- ----- ----- ----- 460 71 3.47 0.126
622531 EAST GERMANY SSK2 PRE 1992 ACQ. BY SCHOTT 10MM ~320 ~351 ~385 ~>1500 (98.9%) ----- 66 3.68 0.133
622531 HIKARI GLASS CO. E-SSK2 2001 EG/P 10MM ~<330(5%) ~345 ~369 ~>2200(93.3%) 437 646  ----- 3.45 0.125
622531 HOYA CORP. BaCED2 1978 H / I 5MM ~<310 (5%) ~335 ~360 ~>700 (99.9%) 555  ----- 3.68 0.133
622531 RUSSIA C227 PRE 1992 H / I 10MM ~<340 (28.4%) ~350 ~379 ~>1100 (98.8%) ----- 63 3.66 0.133
622532 OHARA CORP. BSM22 1996 H / I 10MM ~<320 (11%) ~331 ~353 ~>2200 (92.4%) 530 64 3.68 0.133
622532 OHARA CORP. S-BSM22 1999 P/EG 10MM ~<340 (8%) ~355 ~380 ~>2200 (93.8%) 580 66 3.24 0.117
622532 SCHOTT GLASS TECH. SSK2 1992 I 5MM ~<310 (3%) ~325 ~346 ~>2325.4 (94%) 460 773 62 3.67 0.133
622533 SCHOTT GLASS TECH. NSSK2 2000 P 10MM ~<334 (8%) ~348 ~372 ~>1970 (97.1%) 570 58 3.53 0.128
622567 CHINA ZK10 1996 H / I ----- ----- ----- ----- ----- 555  ----- 3.67 0.133
622567 RUSSIA C125 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 67 3.58 0.130
623382 HAYWARD SCIENTIFIC BF5 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
623531 CORNING-FRANCE C23-53 1991 P 10MM ~<320 (5.1%) ~339 ~369 ~>1800 (97.9%)  ----- 733 62 3.75 0.136
623569 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.58 0.130
623569 CORNING-FRANCE C23-57 1991 P 10MM ~<310 (8.2%) ~331 ~362 ~>1800 (97.8%)  ----- 748 70 3.54 0.128
623569 EAST GERMANY SK10 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 63 3.66 0.133
623569 HOYA CORP. BaCD10 DERIVED  HYPOTHETICAL 1MM*  ----- ~<310 (63.1%) ~329 ~>1550 (99.9%) 555 63 3.67 0.133
623569 HOYA CORP. BaCD10 1998 P 5MM ~<310 (12%) ~326 ~354 ~>1550 (99.6%) 555 63 3.67 0.133
623569 HOYA CORP. E-BaCD10 DERIVED  HYPOTHETICAL 1MM*  ----- ~<290 (63.1%) ~315 ~>1550 (99.9%) 535 67 3.66 0.133
623569 HOYA CORP. E-BaCD10 1998 P/EG 5MM ~<280 (3%) ~310 ~342 ~>1550 (99.7%) 535 67 3.66 0.133
623569 PILKINGTON OPTICAL   DBC623569 1990 H / I 10MM  ------ ~<360 (87.1%) ~367 ~>1000 (99.7%) 520 69 3.66 0.133
623569 PILKINGTON OPTICAL   DBC623569A 2002 EG 5MM  ----- ~<320 (76.4%) ~340 ~>2200.0 (93.8%) 529 70 3.66 0.133
623569 SCHOTT GLASS TECH. SK10 1992 H / I 5MM ~<300 (4%) ~324 ~348 ~>2325.4 (92%) 570 744 70 3.66 0.133
623570 OHARA CORP. S-BSM10 1996 P/EG 10MM ~<310 (8%) ~327 ~356 ~>2200 (91.3%) 550 65 3.60 0.130
623570 SCHOTT GLASS TECH. NSK10 2000 P 10MM ~310 ~332 ~361 ~>1970 (95.4%) 550 80 3.67 0.133
623571 OHARA CORP. BSM10 1990 H / I 10MM ~<310 (2%) ~332 ~362 ~>1060 (99.6%) 540 68 3.65 0.132
623572 HAYWARD SCIENTIFIC DBC6 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
623580 OHARA CORP. L-BSM15 1999 10MM ~<310 (13%) ~324 ~350 ~>700 (99.9%) 570 71 3.52 0.127
623580 SCHOTT GLASS TECH. NSK15 2000 P 10MM ~310 ~334 ~363 ~>1970 (95.9%) 620 67 3.62 0.131
623581 CORNING-FRANCE C23-58 1991 P 10MM ~301 ~323 ~357 ~>1800 (97.9%)  ----- 755 71 3.58 0.130
623581 EAST GERMANY SK15 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 68 3.67 0.133
623581 HOYA CORP. BaCD15 1998 P 5MM ~<280 (6%) ~311 ~344 ~>1550 (99.7%) 595 61 3.55 0.129
623581 HOYA CORP. BaCD15  DERIVED  HYPOTHETICAL 1MM*  ----- ~<290 (63.1%) ~317 ~>1550 (99.9%) 595 61 3.55 0.129
623581 PILKINGTON OPTICAL   DBC623581 1990 H / I 10MM  ----- ~<360 (87.7%) ~367 ~>1000 (99.3%) 590 63 3.44 0.125
623581 PILKINGTON OPTICAL   DBC623581A 2002 EG 5MM  ----- ~<330 (84.2%) ~338 ~>2200.0 (93.5%) 594 59 3.46 0.125
623581 SCHOTT GLASS TECH. SK15 1992 H / I 5MM ~<300 (12%) ~316 ~346 ~>2325.4 (91%) 450 744 69 3.64 0.132
623582 HIKARI GLASS CO. E-SK15 2001 EG/P 10MM ~<300(2%) ~326 ~353 ~>2200(94.2%) 471 681  ----- 3.66 0.133
623582 OHARA CORP. BSM15 1990 H / I 10MM ~<310 (3%) ~330 ~357 ~>700 (99.7%) 540 70 3.65 0.132
623582 OHARA CORP. S-BSM15 1996 P/EG 10MM ~<330 (13%) ~342 ~367 ~>2200 (91.8%) 560 65 3.60 0.130
624359 CHINA F5 1996 H / I ----- ----- ----- ----- ----- 360 95 3.66 0.133
624359 RUSSIA C320 PRE 1992 H / I 10MM ----- ~<380 (89.0%) ~383 ~>1100 (99.7%) ----- 73 3.67 0.133
624365 OHARA CORP. PBM10 1990 H / I 10MM ~320 ~338 ~365 ~>1060 (99.7%) 430 83 3.62 0.131
624368 CHINA F12 1996 H / I ----- ----- ----- ----- -----  ----- 77 3.62 0.131
624469 CORNING-FRANCE C24-47 1991 P 10MM ~<320 (3.3%) ~336 ~367 ~>1800 (97.9%)  ----- 690 58 3.45 0.125
624470 EAST GERMANY BaF8 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (14.6%) ~360 ~394 ~>1500 (98.6%) ----- 71 3.60 0.130
624470 HIKARI GLASS CO. E-BAF8 2001 EG/P 10MM ~<350 (12%) ~362 ~387 ~>700(99.9%) 511 640  ----- 3.14 0.114
624470 SCHOTT GLASS TECH. BaF8 1992 I 5MM ~<320 (10%) ~331 ~350 ~>2325.4 (95.2%) 460 737 70 3.67 0.133
624471 HOYA CORP. BAF8 DERIVED  HYPOTHETICAL 1MM*  ---- ~<330 (83.3%) ~336 ~>1550 (99.9%) 535 73 3.66 0.133
624471 HOYA CORP. BAF8 1998 P 5MM ~<320 (7%) ~333 ~352 ~1550 (99.7%) 535 73 3.66 0.133
624471 HOYA CORP. EBAF8 DERIVED  HYPOTHETICAL 1MM*  ----- ~<340 (77.7%) ~351 ~>1550 (99.9%) 515 80 3.32 0.120
624471 HOYA CORP. EBAF8 1998 P/EG 5MM ~<330 (6%) ~348 ~372 ~>1550 (99.7%) 515 80 3.32 0.120
624471 OHARA CORP. BAM8 1990 I 10MM ~<330 (10%) ~344 ~374 ~>700 (99.7%) 490 63 3.62 0.131
625353 RUSSIA C331 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 106 3.59 0.130
625356 CHINA F6 1996 H / I ----- ----- ----- ----- ----- 380 95 3.60 0.130
625356 EAST GERMANY F7 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (40.8%) ~345 ~376 ~>1500 (99.2%) ----- 91 3.61 0.131
625356 HOYA CORP. F7 1978 H / I 5MM  -----  -----  -----  ----- 415  ---- 3.66 0.133
625356 SCHOTT GLASS TECH. F7 1992 I 5MM ~310 ~328 ~347 ~>1970.1 (95.4%) 360 580 98 3.62 0.131
626356 CORNING-FRANCE C26-36 1991 P 10MM ~<320 (4.6%) ~336 ~357 ~>1800 (96.6%)  ----- 587 87 3.65 0.132
626357 CHINA F13 1996 H / I ----- ----- ----- ----- ----- 365 85 3.66 0.133
626357 HAYWARD SCIENTIFIC DF7 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
626357 HOYA CORP. EF1 DERIVED  HYPOTHETICAL 1MM*  ----- ~<360 (82.2%) ~367 ~>1550 (99.9%) 550 86 2.70 0.098
626357 HOYA CORP. EF1 1998 P/EG 5MM ~<350 (6%) ~364 ~383 ~>1550 (99.6%) 550 86 2.70 0.098
626357 HOYA CORP. F1 DERIVED  HYPOTHETICAL 1MM*  ---- ~<320 (63.1%) ~336 ~>1550 (99.9%) 435 81 3.68 0.133
626357 HOYA CORP. F1 1998 P 5MM ~<320 (7%) ~333 ~349 ~>1550 (99.8%) 435 81 3.68 0.133
626357 HOYA CORP. F1 1978 H / I 5MM ~<320 (13%) ~330 ~350 ~>700 (99.9%) 435 81 3.65 0.132
626357 OHARA CORP. PBM1 1990 I 10MM ~<320 (2%) ~336 ~359 ~>1060  (99.9%) 400 89 3.65 0.132
626357 OHARA CORP. S-TIM1 1996 P/EG 10MM ~<360 (9%) ~371 ~392 ~>2200 (91.7%) 530 81 2.71 0.098
626357 PILKINGTON OPTICAL   DF626357 1990 H / I 10MM  ----- ~<360 (83.7%) ~372 ~>1000 99.5%) 410 84 3.66 0.133
626357 SCHOTT GLASS TECH. F1 1992 I 5MM ~<320 (7%) ~330 ~350 ~>2325.4 (93%) 350 593 87 3.65 0.132
626358 HIKARI GLASS CO. E-F1 2001 EG/P 10MM  ----  ----  ----  ---- 476 634  ----- 2.72 0.098
626390 SCHOTT GLASS TECH. BaSF1 1992 I 5MM ~<334.1 (41%) ~338 ~361 ~>2325.4 (94%) 400 658 85 3.66 0.133
626391 CHINA BAF8 1996 H / I ----- ----- ----- ----- ----- 425 81 3.68 0.133
626391 EAST GERMANY BaSF1 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (18.4%) ~355 ~395 ~>1500 (99.3%) ----- 91 3.67 0.133
626391 HOYA CORP. BaFD1 1978 H / I 5MM ~<320 (10%) ~333 ~358 ~>700 (99.9%) 460 83 3.67 0.133
626391 RUSSIA C229 PRE 1992 H / I 10MM ~<340 (30.0%) ~349 ~378 ~>1500 (9.1%) ----- 83 3.67 0.133
626392 OHARA CORP. BAM21 1990 I 10MM ~<330 (18%) ~339 ~370 ~>1060 (99.8%) 450 82 3.63 0.131
628594 RUSSIA C124 PRE 1992 H / I ----- ----- ----- ----- ----- ----- 69 3.66 0.133
632570 HIKARI GLASS CO. E-SK10 2001 EG/P 10MM  ----  ----  ----  ---- 547 680  ----- 3.57 0.129
635350 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.70 0.134
635368 RUSSIA C242 PRE 1992 H / I 10MM ~<340 (5.5%) ~364 ~396 ~>1100 (99.3%) ----- 74 3.67 0.133
636350 HAYWARD SCIENTIFIC DF6 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
636353 HOYA CORP. F6 1978 H / I 5MM ~<320 (5%) ~338 ~365 ~>700 (99.9%) 435  ----- 3.74 0.135
636353 SCHOTT GLASS TECH. F6 1992 I 5MM ~<320 (10%) ~330 ~350 ~>2325.4 (94%) 360 605 85 3.76 0.136
636354 CHINA F7 1996 H / I ----- ----- ----- ----- ----- 375 84 3.76 0.136
636354 OHARA CORP. PBM6 1990 H / I 10MM ~<330 (10%) ~343 ~368 ~>1060 (99.8%) 420 85 3.74 0.135
636354 OHARA CORP. S-TIM6 1999 EG 10MM ~<370 (14%) ~380 ~411 ~>1000 (99.9%) 530 83 2.79 0.101
637353 CORNING-FRANCE C37-35 1991 P 10MM ~<320 (9.9%) ~337 ~360 ~>1800 (97.4%)  ----- 607 65 3.75 0.136
637555 HAYWARD SCIENTIFIC DBC5 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
638424 CORNING-FRANCE C38-42 1991 NA 10MM ~<320 (12.9%) ~336 ~368 ~>1000 (99.8%) 556  -----  ----- 3.22 0.117
638555 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.59 0.130
639449 HIKARI GLASS CO. E-BAF12 2001 EG/P 10MM ~<350 (6%) ~364 ~387 ~>2200(92.5%) 535 635  ----- 3.22 0.117
639449 OHARA CORP. BAM12 1990 H / I 10MM ~<330 (5%) ~347 ~377 ~>1060 (99.6%) 470 76 3.80 0.138
639449 OHARA CORP. S-BAM12 1996 P/EG 10MM ~<350 (13%) ~360 ~385 ~>2200 (93.2%) 550 76 3.18 0.115
639451 HOYA CORP. BaF12 1978 H / I 5MM ~<330 (6%) ~348 ~370 ~>700 (99.9%) 525  ----- 3.82 0.138
639452 CHINA ZBAF13 1996 H / I ----- ----- ----- ----- ----- 455 67 3.60 0.130
639452 SCHOTT GLASS TECH. BaF12 1992 H / I 5MM  ----- ~<350 (59%) ~385 ~>2325.4 (95%) 460  ----- 68 3.60 0.130
639554 OHARA CORP. BSM18 1990 H / I 10MM ~330 ~354 ~384 ~>700 (99.6%) 520 71 3.67 0.133
639554 OHARA CORP. S-BSM18 1996 P/EG 10MM ~330 ~349 ~373 ~>2200 (91.4%) 540 69 3.69 0.134
639554 PILKINGTON OPTICAL   DBC639554 1990 H / I 10MM  ----- ~<360 (61.9%) ~368 ~>1000 (99.5%) 500 67 3.70 0.134
639554 PILKINGTON OPTICAL   DBC639554A 2002 EG 5MM  ----- ~<340 (62.3%) ~376 ~>2200.0 (93.1%) 542 71 3.70 0.134
639554 SCHOTT GLASS TECH. NSK18 2000 P 10MM ~320  ~345 ~370 ~>1970 (95.9%) 610 64 3.64 0.132
639554 SCHOTT GLASS TECH. SK18A 1992 H / I 5MM ~<334.1 (36%) ~339 ~362 ~>1970.1 (97.8%) 610   ----- 64 3.64 0.132
639555 CHINA ZK11 1996 H / I ----- ----- ----- ----- ----- 590 62 3.66 0.133
639555 CORNING-FRANCE C39-56 1991 P 10MM ~<280 (2.7%) ~321 ~355 ~>1800 (97.7%)  ----- 741 63 3.08 0.112
639555 HIKARI GLASS CO. S-SK18 2001 EG/P 10MM  ----  ----  ----  ---- 488 684  ----- 3.67 0.133
639555 HOYA CORP. BaCD18 DERIVED  HYPOTHETICAL 1MM*  ----- ~<320 (72.5%) ~335 ~>1550 (99.9%) 590 69 3.66 0.133
639555 HOYA CORP. BaCD18 1998 P 5MM ~<320 (19%) ~331 ~356 ~1550 (99.6%) 590 69 3.66 0.133
639555 SCHOTT GLASS TECH. SK52 1992 H / I 5MM ~<320 (6%) ~337 ~350 ~>700 (99.8%) 520  ----- 60 3.30 0.119
639556 EAST GERMANY SK18 PRE 1992 ACQ. BY SCHOTT ----- ----- ----- ----- ----- ----- 64 3.69 0.134
640345 OHARA CORP. PBM27 1990 I 10MM ~<330 (16%) ~339 ~362 ~>1060 (99.9%) 400 88 3.78 0.137
640345 OHARA CORP. S-TIM27 1996 P/EG 10MM ~<360 (5%) ~372 ~395 ~>2200 (93.6%) 560 80 2.76 0.100
640346 EAST GERMANY SF7 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (28.8%) ~349 ~380 ~>1500 (99.6%) ----- 73 3.78 0.137
640346 HIKARI GLASS CO. E-SF7 2001 EG/P 10MM ~<360(3%) ~375 ~398 ~>2200(90.6%) 498 626  ----- 2.77 0.100
640346 HOYA CORP. EDF7 1998 P/EG 5MM ~<350 (3%) ~366 ~385 ~>1550 (99.7%) 540 87 2.75 0.100
640346 HOYA CORP. EFD7 DERIVED  HYPOTHETICAL 1MM*  ---- ~<360 (78.6%) ~369 ~>1550 (99.9%) 540 87 2.75 0.100
640346 HOYA CORP. FD7 DERIVED  HYPOTHETICAL 1MM*  ------ ~<330 (72.5%) ~340 ~>1550 (99.9%) 410 85 3.79 0.137
640346 HOYA CORP. FD7 1998 P 5MM ~<330 (19%) ~338 ~358 ~>1550 (99.7%) 410 85 3.79 0.137
640346 SCHOTT GLASS TECH. SF7 1992 H / I 5MM ~<320 (2%) ~332 ~350 ~>2325.4 (94%) 350 608 79 3.80 0.138
640483 CHINA ZBAF2 1996 H / I ----- ----- ----- ----- ----- 445 60 3.83 0.139
640483 RUSSIA C231 PRE 1992 H / I 10MM ~<340 (12.4%) ~358 ~395 ~>1500 (98.8%) ----- 61 3.82 0.138
640597 SCHOTT GLASS TECH. LaKL21 1992 I 5MM ~<290 (27%) ~308 ~348 ~>1970.1(98.1%) 590  ----- 61 2.97 0.108
640601 HIKARI GLASS CO. E-LAK01 2001 EG/P 10MM ~<300(2%) ~338 ~375 ~>700(99.7%) 622 680  ----- 3.01 0.109
640601 OHARA CORP. BSM81 1990 H / I 10MM ~<320 (15%) ~341 ~375 ~>700 (99.6%) 650 58 3.06 0.111
640601 OHARA CORP. S-BSM81 1996 P/EG 10MM ~<300 (2%) ~338 ~374 ~>2000 (96.1%) 670 89 3.06 0.111
640601 SCHOTT GLASS TECH. NLAK21 2000 P/EG 10MM ~<310 (6%) ~331 ~364 ~>1970 (95.0%) 600  ----- 68 3.74 0.135
640602 HOYA CORP. LaCL6 1978 H / I 5MM ~<290 (16%) ~325 ~360 ~>700 (99.9%) 680  ----- 3.65 0.132
640602 HOYA CORP. LaCL60 DERIVED  HYPOTHETICAL 1MM*  ----- ~<280 (77.7%) ~305 ~>1550 (99.9%) 665 60 3.02 0.109
640602 HOYA CORP. LaCL60 1998 P 5MM ~<280 (28%) ~<296 ~340 ~>1550 (99.7%) 665 60 3.02 0.109
641568 HOYA CORP. LaCL1 1978 H / I 5MM ~<310 (5%) ~330 ~360 ~>700 (99.9%) 585  ----- 3.59 0.130
641569 OHARA CORP. BSM93 1990 H / I 10MM ~<330 (12%) ~341 ~365 ~>700 (99.7%) 550 67 3.70 0.134
641569 OHARA CORP. S-BSM93  ---- EG  ------  -----  ------  -----  ------ 550 67 3.70 0.134
641601 CHINA LAK4 1996 H / I ----- ----- ----- ----- ----- 470 66 3.71 0.134
641601 CORNING-FRANCE C41-60 1991 P 10MM ~290  ~335 ~370 ~>1800 (97.9%)  ----- 716 65 3.74 0.135
641601 PILKINGTON OPTICAL   LAC641601B 2002 I 5MM  ----- ~<360 (88.0%) ~365 ~>1000 (99.6%) 630 55 3.37 0.122
641601 SCHOTT GLASS TECH. LaK21 1992 H / I 5MM ~<290 (4%) ~320 ~354 ~>1970.1 (97.5%) 600 68 3.74 0.135
642580 SCHOTT GLASS TECH. LaKN6 1992 I 5MM ~<290 (3%) ~324 ~356 ~>1970.1 (97.9%) 570 70 3.80 0.138
642581 CORNING-FRANCE C42-58 1991 P 10MM ~<320 (20.6%) ~337 ~367 ~>1800 (98.1%)  ----- 711  ----- 3.82 0.138
643478 EAST GERMANY BaF9 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (8.0%) ~359 ~395 ~>1500 (98.9%) ----- 58 3.86 0.140
643479 HOYA CORP. BaF9 1978 H / I 5MM ~<320 (5%) ~340 ~370 ~>700 (99.9%) 520 62 3.83 0.139
643479 OHARA CORP. BAM9 1990 I 10MM ~<330 (4%) ~348 ~377 ~>1060 (99.6%) 490 69 3.85 0.139
643480 SCHOTT GLASS TECH. BaF9 1992 I 5MM ~<320 (5%) ~327 ~363 ~>2325.4 (94%) 460  ----- 65 3.85 0.139
643580 HOYA CORP. LaC6 1978 H / I 5MM ~<280 (7%) ~315 ~350 ~>700 (99.9%) 625  ----- 3.57 0.129
643580 PILKINGTON OPTICAL   LAC643580 1990 H / I 10MM  ----- ~<360 (92.2%) ~<360 (92.2%) ~>1000 (99.6%) 560 72 3.76 0.136
643580 SCHOTT GLASS TECH. LaKN6 1992 I 5MM ~<290(3%) ~324 ~356 ~>2325.4(90%) 460 733 70 3.80 0.138
643584 OHARA CORP. BSM36 1990 H / I 10MM ~<300 (8%) ~329 ~364 ~>700 (99.9%) 550 64 3.66 0.133
643584 OHARA CORP. S-BSM36  ----- EG  -------  -----  -------  -----  ---- 550 64 3.64 0.132
644360 SCHOTT GLASS TECH. NBASF2 2000 P/EG 10MM ~<365 (16%) ~376 ~403 ~>1970 (97.1%) 580 71 3.15 0.114
645408 HOYA CORP. ADF355 1978 H / I 5MM  -----  -----  -----  ----- 465 62 3.48 0.126
645408 OHARA CORP. BPH35 1990 I 10MM ~320 ~353 ~388 ~>700 (99.8%) 470 48 3.46 0.125
645480 HAYWARD SCIENTIFIC DBF4 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
646341 SCHOTT GLASS TECH. SF16 1992 I 5MM ~<320 (2%) ~337 ~356 ~>2325.4 (93%) 340 604 84 3.85 0.139
648338 CHINA ZF1 1996 H / I ----- ----- ----- ----- ----- 410 84 3.85 0.139
648338 HIKARI GLASS CO. E-SF2 2001 EG/P 10MM ~<360(3%) ~375 ~397 ~>2200(90.6%) 602 624  ----- 2.77 0.100
648338 HOYA CORP. EFD2 DERIVED  HYPOTHETICAL 1MM*  ----- ~<360 (78.6%) ~369 ~>1550 (99.9%) 525 88 2.77 0.100
648338 HOYA CORP. FD12 1978 H / I 5MM ~<350 (11%) ~360 ~380 ~>700 (99.9%) 415 81 3.74 0.135
648338 HOYA CORP. FD2 DERIVED  HYPOTHETICAL 1MM*  ----- ~<330 (75.5%) ~339 ~>1550 (99.9%) 410 86 3.85 0.139
648338 HOYA CORP. FD2 1998 P 5MM ~<330 (24%) ~336 ~353 ~>1550 (99.6%) 410 86 3.85 0.139
648338 OHARA CORP. PBM22 1990 I 10MM ~<330 (8%) ~343 ~365 ~>700 (99.8%) 400 88 3.85 0.139
648338 OHARA CORP. PBM32 1990 H / I 10MM ~<330 (8%) ~343 ~365 ~>700 (99.8%) 410 86 3.85 0.139
648338 OHARA CORP. S-TIM22 1996 P/EG 10MM ~<360 (4%) ~374 ~396 ~>2200 (93.4%) 560 83 2.79 0.101
648338 SCHOTT GLASS TECH. SF12 1992 I 5MM ~<350 (17%) ~360 ~379 ~>2325.4 (94%) 360 611 78 3.74 0.135
648339 CORNING-FRANCE C48-34 1991 P 10MM ~<320 (4%) ~340 ~364 ~>1800 (96.5%) 354 583 82 3.86 0.140
648339 EAST GERMANY SF2 PRE 1992 ACQ. BY SCHOTT 10MM ~<340 (25.5%) ~371 ~386 ~>1500 (99.5%) ----- 82 3.85 0.139
648339 PILKINGTON OPTICAL   EDF648339 1990 H / I 10MM  -----  -----  -----  ------ 370 79 3.86 0.140
648339 PILKINGTON OPTICAL   EDF648339A 2002 EG 5MM  ----- ~<340 (69.4%) ~358 ~>2200.0 (94.9%) 376 84 3.86 0.140
648339 RUSSIA C341 PRE 1992 H / I 10MM  ----- ~<380 (84.0%) ~390 ~>1500 (99.3%) ----- 82 3.86 0.140
648339 SCHOTT GLASS TECH. SF2 2000 P 10MM ~<334 (11%) ~345 ~368 ~>1970 (95.0%) 410  ----- 84 3.86 0.140
648462 CORNING-FRANCE C48-46 1991 P 10MM ~<320 (2%) ~345 ~384 ~>1800 (98.3%)  ---- 701 60 3.65 0.132
649316 RUSSIA C357 PRE 1992 H / I 10MM ~<380 (39.8%) ~385 ~412 ~>1500 (99.3%) ----- 97 3.14 0.114
649338 BAUSCH & LOMB ----- PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- 3.91 0.142
649339 HAYWARD SCIENTIFIC DF4 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
649358 HAYWARD SCIENTIFIC BF3 PRE-1979 NA ----- ----- ----- ----- ----- ----- ----- ----- -----
649530 HOYA CORP. BaCED20 DERIVED  HYPOTHETICAL 1MM*  ----- ~<330 (63.1%) ~350 ~>700 (99.9%) 550 75 3.74 0.135
649530 HOYA CORP. BaCED20 1998 P 5MM ~<330 (12%) ~346 ~372 ~>700 (99.9%) 550 75 3.74 0.135
649530 HOYA CORP. E-BaCED20 DERIVED  HYPOTHETICAL 1MM*  ----- ~<290 (63.1%) ~322 ~>1550 (99.9%) 580 70 3.68 0.133
649530 HOYA CORP. E-BaCED20 1998 P/EG 5MM ~<280 (2%) ~316 ~348 ~>1550 (99.8%) 580 70 3.68 0.133
649530 OHARA CORP. BSM71 1990 H / I 10MM ~<340 (8%) ~357 ~385 ~>1060 (99.6%) 560 71 3.74 0.135
649530 OHARA CORP. S-BSM71 1996 P/EG 10MM ~340 ~351 ~376 ~>2200 (92.5%) 560 71 3.74 0.135